1·High temperature gas solid suspension reactor was used to simulate decomposition of cement raw meal.
应用高温气固悬浮实验台对水泥生料在预分解炉中分解动力学的过程进行了模拟实验。
2·The burnability of the cement raw meal prepared by shale or yellow-sand has been studied in this paper.
本文研究了以黄沙或页岩代替粘土质原料配制水泥生料的易烧性。
3·The effect factor of fly ash as a raw material on the raw meal grindability has been studied in this paper.
对粉煤灰代替粘土配料时，影响生料易磨性的因素进行了研究。
4·It is theoretically possible in using SO3 of high sulfur coal instead of gypsum for raw meal proportioning.
利用高硫煤中的SO_3替代石膏中的SO_3进行生料配料，在理论上是可行的。
5·Small pelletized raw meal with smooth surface were obtained through the modification of pelletization process.
通过改进成球工艺，使料球小而光滑；
6·The present invention relates to building material, and is especially preparation of raw meal for Portland cement.
本发明涉及一种建筑材料的制备方法，特别是涉及硅酸盐水泥生料的制备。
7·Compared with that of limestone, the properties of siliceous material will have more influence on the burnability of raw meal.
与石灰石相比，硅质原料性质对生料易烧性影响更大。
8·Weighed raw meal will be fed to pre-heater. After heating, it will be discomposed in decomposition furnace and then fed to kiln.
来自均化库的合格生料计量后进入预热器，逐级预热后进入分解炉，分解后的生料再进入回转窑内煅烧。
9·Besides, calcium carbide slag is favorable to improve burn-ability of raw meal, and to reduce heat consumption of clinker for energy saving.
同时，电石渣有利于改善生料易烧性，降低熟料热耗，节约能源。
10·During commissioning, problems like low qualified raw meal modulus, accretion within preheating system and ESP dust discharge failure are all solved.
在生产调试中出现的生料率值合格率偏低、窑尾结皮、电除尘器排灰问题均得到了较好的解决。